Prepare the tapered drill rod before use
Related products Link:
1. Check the appearance quality of the drill rod. For example, whether there are defects on the surface of the drill rod that affect the use, whether the flatness of the drill rod is good, etc., some of these factors are caused by the handling process. Users of slightly bent drill rods can solve it on site. Please do not use hammering when straightening.
2. Check whether the drill rod and the drill bit fit well, otherwise, the drill may break slightly. Pay attention to the wear of the drill bit blade. Continue to use the abnormally damaged drill bit on the one hand will cause the drill bit to be scrapped in advance, and on the other hand, it will greatly reduce the service life of the drill rod.
3. Check the fit of the drill rod, the rock drill and the connecting parts. Sometimes the early failure of the drill rod is caused by the wear of the rock drill accessories. For example, the hexagonal sleeve of the pneumatic rock drill is severely worn. Fracture, on the other hand, has the effect of accelerating wear on the internal parts of the rock drill.
4. Check whether the water hole of the drill rod is unblocked. Do not use the drill rod with impermissible water hole. In this case, the manufacturer will provide free replacement.
In order to meet the needs of mine production and engineering construction, domestic hydraulic rock drilling machinery has been introduced. Heavy-duty hydraulic drilling rigs have been used in mines, It has been widely used in water conservancy, tunnels, highways, railways and other rock drilling operations, and the domestic heavy-duty drill market has further expanded. In the entire drilling process, in addition to the raw material factors, the heat treatment process is the most critical factor in determining the quality of the drill rod.
The thread failure of the drill rod is mainly due to dynamic wear and impact wear, which leads to the failure of the drill rod. Existence, it directly affects product quality and is related to the credibility and survival of the enterprise. Wear, corrosion and fracture are the three main forms of drill rod failure. Among them, wear failure caused by friction is the main reason for the failure of drill rods. About 70%-80% of drill rods are damaged. Caused by various forms of wear. The basis for the selection of the heat treatment process of drill rods is the steel used for steel drill tools. With the development of impact rock drilling machinery, various series and categories have been formed.
In the production of drill rods, the correct choice of steel type is possible to select a heat treatment process that can fully utilize the advantages of the steel type to ensure the quality and life of the drill rod. Different steel grades have different better heat treatment processes.
The selection of the heat treatment process of the drill rod should follow the principles of economy, rationality and feasibility. The current development of heat treatment technology is changing with each passing day. In addition to conventional heat treatment, induction heating, chemical heat treatment, and vacuum heat treatment, there are also high-energy beams (laser, electron beam, etc.) ) Heat treatment, physical vapor deposition and chemical vapor deposition, ion implantation, spraying and other new surface strengthening heat treatment technologies.
Drill rods are long and slender rods, so the overall treatment has great limitations. Often a heat treatment process cannot meet the basic requirements of each part of the drill rod. Several heat treatment processes should be selected to treat each part separately. How to choose a heat treatment process suitable for the basic requirements of drill rods among the many heat treatment technologies, it is necessary to consider economy, rationality and feasibility.